HRB400/HRB400E Deformed Steel Rebar

HRB400 is a steel reinforcement material with high strength and good plasticity. HR stands for "hot rolling", which essentially refers to the heating and rolling process of steel bars in the production process. B represents that its yield strength is 400 megapascals (MPa) higher than that of ordinary carbon steel.

  Product Description

1. High strength: The yield strength of HRB400 steel bars is 400 MPa, which has higher strength and tensile properties compared to general carbon steel, and can effectively increase the bearing capacity of concrete components.
2. Good plasticity: HRB400 steel bars have good toughness and elongation after being subjected to stress, and can maintain high strength even if bending and deformation occur.
3. Good welding performance: HRB400 steel bars have good weldability and can be welded with other steels, making them convenient for use in construction.
4. Weather resistance: HRB400 steel bars have good weather resistance and can be used for a long time in harsh weather conditions, making them less susceptible to oxidation and corrosion.
5. Simple construction: The shape of HRB400 steel bars is relatively simple, usually flat or circular, which is convenient for processing and use.


Product Parameters

Product Name

HRB400/HRB400E Deformed Steel Rebar

Standard

EN/DIN/JIS/ASTM/BS/ASME/AISI, etc.

Common Round Bar Specifications

3.0-50.8 mm, Over 50.8-300mm

Flat Steel Common Specifications

6.35x12.7mm, 6.35x25.4mm, 12.7x25.4mm

Hexagon Bar Common Specifications

AF5.8mm-17mm

Square Bar Common Specifications

AF2mm-14mm, AF6.35mm, 9.5mm, 12.7mm, 15.98mm, 19.0mm, 25.4mm

Length

1-6meters, Size Accept Custom

Diameter(mm)

Hot Rolling Round Bar

25-600

Cold Rolling Square Bar

6-50.8

Hot Rolling Square Bar

21-54

Cold Rolling Hexagon Bar

9.5-65

Cold Rolling Round bar

6-101.6

Forged Rebar

200-1000

Surface Process

Bright, Polished, Black

Other Services

Machining(cnc), Centerless Grinding(cg), Heat Treatment, Annealing, Pickling, Polishing, Rolling, Forging, Cutting, Bending, Small Machining, etc.


Chemical Composition

Carbon

Silicon

Manganese

Sulphur

Phosphorus

0.25%

0.80%

1.6%

0.045%

0.045%


Mechanical Properties

Chinese Rebar Code

Yield Strength (Mpa）

Tensile Strength (Mpa）

Carbon Content

HRB400, HRBF400, HRB400E, HRBF400E

400

540

≤0.25

HRB500, HRBF500, HRB500E, HRBF500E

500

630

≤0.25

HRB600

600

730

≤ 0.28


Scope of Application

Widely used in houses, bridges, roads, especially railways and other civil engineering.


  Product Show

Related products

Message

Requiredwrong format
Requiredwrong format
Requiredwrong format
Required
Privacy Policy

© Hanwu Iron and Steel (Shandong) Co., Ltd.Rights Reserved